unannealed

基本解释

However, the value of magnetoresistance increased apparently after annealing and was 1.74 times the unannealed sample.
而退火后磁电阻值则明显增加，是未退火时的1.;74倍；
From the PL measurement the near band edge(NBE) emission and deep-level(DL) emission are observed in unannealed AZO thin films.
未退火样品的光致发光(PL)谱由361 nm附近的紫外带边发射峰和500 nm附近的深能级发射峰组成。
The experimental results indicated that the film resistivity of the sample annealed was reduced significantly and only one 3.17 of the unannealed.
实验结果表明：退火后样品的薄膜电阻率显著减小，是未退火样品薄膜电阻率的3.;17分之一；
XRD structural analysis shows thatpeak intensity of the annealed sample is greater than that of the unannealed one which demonstrated an increase of crystallinity.
XRD结构分析显示，退火后薄膜样品的峰值强度大于未退火样品的强度，说明样品结晶度增强。
MAGNETOTRANSPORT STUDY OF TWO-DIMENSIONAL ELECTRON GAS IN ANNEALED AND UNANNEALED MM-HEMT MATERIAL
退火与未退火MM-HEMT材料中二维电子气的磁输运特性研究